Silver Brazing Alloys Bearing Cadmium

Product	Composition %					Melting Range		Specifications
	Silver	Copper	Zinc	Cadmium	Nickel	Solidus 'c	Liquidus 'c	IS:2927	BS:1845	DIN:8513	AWS:A5.8
VE 50%-Cd	50	16	15	19	-	629	637	BaCuAg10	AG1	L-Ag50Cd	BAg-1a
VE 50N-Cd	50	16	16	15	3	634	688	BaCuAg12	AG9	L-Ag50CdNi	BAg-3
VE 45%-Cd	45	15	17	23	-	605	620	BaCuAg15	-	-	BAg-1
VE 43%-Cd	43	16	19	22	-	610	620	BaCuAg16A	AG2	-	-
VE4 0%-Cd	40	18	21	21	-	593	628	-	AG10	L-Ag40Cd	-
VE 35%-Cd	35	26	18	21	-	610	702	BaCuAg20	AG11	L-Ag34Cd	BAg-2
VE 30%-Cd	30	29	21	20	-	610	700	-	AG12	L-Ag30Cd	BAg-2a
VE 25%-Cd	25	35	26	14	-	600	715	-	-	-	BAg-27
VE 20%-Cd	20	39	29	12	-	603	755	-	-	L-Ag20Cd	-

VE 50% Cd & VE 50N Cd
For brazing tungsten carbide tips to rock drills, milling cutters, cutting and shaping tools, also suitable for brazing steels which are difficult to "Wet" such as stainless steels. (Flame-neutral)
VE 45% Cd  VE 43% Cd & VE 40%  Cd
These alloys are an ideal composition for economy in brazing operation requiring a low temperature, quick amd complete penetration, and neat joints of high strength that need little or no finishing. These alloys are essentially used where joints to employ fitted or where it is desired are closely brazing alloys that will be effective in the widest possible range of application. They provide satisfactory results on steel, copper, brass, gun metal, tin bronzes, aluminum and manganese bronzes, copper-nickel alloys and nickel silvers of all types. (Flame-neutral).
VE 35% Cd, VE 30% Cd, VE 25% Cd & VE 20% Cd
Alloys for general engineering metals with excellent capillary flow with better ductility for filling gaps

Product	Composition %						Melting Range		Specifications
	Silver	Copper	Zinc	Manganese	Nickel	Tin	Solidus      'c	Liquidus       'c	IS:2927	BS:1845	DIN:8513	AWS:A5.8
VE 60%	60	29	11	-	-	-	688	732	BaCuAg6	-	-	-
VE 55%	55	22	18	-	-	5	620	653	BaCuAg8	-	-	-
VE 50%	50	34	16	-	-	-	688	774	BaCuAg9	-	-	Bag-6
VE 49%	49	16	23	7.5	4.5	-	625	705	-	AG18	L-Ag49	Bag-22
VE 45%	45	29	26	-	-	-	677	743	BaCuAg14	AG15	L-Ag44	Bag-5
VE 43%	43	37	20	-	-	-	688	765	BaCuAg16	AG5	-	-
VE 40%	40	30	28	-	2	-	660	779	BaCuAg18	-	-	Bag-4
VE 30%	30	36	32	-	2	-	690	760	-	-	-	-
VE 25%	25	41	34	-	-	-	680	795	-	AG17	L-Ag25	-

Product	Composition %					Melting Range		Specifications
	Copper	Zinc	Silicon	Manganese	Nickel	Solidus      'c	Liquidus       'c	IS:2927	BS:1453
VE SILICON BRONZE	60	39.7	0.3	-	-	875	905	SC6	C2
VE MANGANESE BRONZE	60	39.6	0.2	0.2	-	895	920	SC8	C4
VE NICKEL BRONZE	51	39.7	0.3	-	10	910	925	SC9	C5

VE Silicon Bronze
For brazing of tubular and sheet metal joints of steel, copper, galvanized iron, fusion welding of brass & bronzes.
VE Manganese Bronze
For braze welding cast and malleable iron. They can also be used for building up of worn surfaces.
VE Nickel Bronze
For braze welding steel or malleable iron. Building up worn surfaces and welding copper-zinc-nickel alloys of similar composition.